Stainless Steel Filler Rod Chart

Type 347 stainless steel filler metal is ideal for 347 and 321 base materials because it matches these stabilized grades.

Stainless steel filler rod chart.

Cg 12 is the cast equivalent of 309. Look at the chart above to find out what 11 indicates. Flux cored wires gas flux cored wires self megafil seamless wire. Stainless steels welding aws e316l 16 stainless steel electrodes tig welding wire tungsten inert gas should i use 4043 or 5356 filler alloy stainless steel electrode chart trinitystainless steel welding filler metal selection chartstick electrode and welding basicsfiller metals for welding stainless steel ldx2101 s32205 2304 254smo 654smo 301 304 316 317l 904l 304h 153ma.

For stainless sheet metal one size lower than you would use for carbon steel seems to help because typically less amperage is used on stainless steel than on carbon steel. Stainless steel metallurgical groups austenitic. Type 321 is available on a limited basis as solid and cored wire. Type 347 can also be welded with type 308h filler.

The next chart below is similar to the one above but it gives you more detail on the six top arc welding rods. Metal cored wires gas solid wires. The attached tables provide generally accepted electrode selections for the base materials shown along with process areas that need special consideration. All are essentially non magnetic.

Some 308l applications may be substituted with 309l filler metal but 316l or 316 applications generally require molybdenum and 309l contains no molybdenum. The most common types of austenitic stainless are the uns s20000 and s30000 alloys. Cf 8c is the cast equivalent. Coating welding positions current and tensile strength for each arc welding rod.

Stainless filler metal selector guide aisi type number 442 446 430f 430 fse 430 431 501 502 416 416 se 403 405 410 420 414 321 348 347 317 316l 316 314 310 310s 309 309s. Two problems are associated with welds in the austenitic stainless steels. Revision 01 06 2014 weld filler metal selection chart for shielded metal arc welding smaw for various metal combinations. They can be hardened by cold working but not by heat treatment.

For aluminum the same rule applies to sheet metal roughly. The austenitic group contains chromium and nickel as the primary alloying elements and are the most widely used. But in my experience. 1 sensitization of the weld heat affected.

At low amperage a large rod chills the puddle a lot and can cause a very irregular bead. Aluminum tig welding rod chart hoskin advances in automatic hot wire gtaw tig welding arc hines inc welding rod chart reading the numbers its ysis and welding princess auto stainless steel welding filler metal selection chart.